Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO<sub>2</sub>

Andry Tahina Rabeharitsara; Ando Princia Randriamalala; Nambinina Richard Randriana; Baholy Robijaona; Marie Hanitriniaina Ratsimba

doi:doi:10.11648/j.ajpst.20220802.12

Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO₂

Andry Tahina Rabeharitsara, Ando Princia Randriamalala, Nambinina Richard Randriana, Baholy Robijaona, Marie Hanitriniaina Ratsimba

Published in American Journal of Polymer Science and Technology (Volume 8, Issue 2)

Received: 12 July 2022 Accepted: 27 July 2022 Published: 5 August 2022

Views: Downloads:

Download PDF

Share This Article

Twitter
Linked In
Facebook

Abstract

The valorization of pozzolana into pn-pozzolana used as water softening was studied. This article treated particularly the valorization of the pn-pozzolana and pn-SiO₂ by adding iron-Fe atoms to give the Fe-pn-pozzolana and Fe-pn-SiO₂. Two synthesis procedures were used with the ironIIethoxide Fe(OEt)₂ as precursor material of the iron-Fe atoms deposits on the pn-pozzolana: first there was the solid-solid synthesis where the pn-pozzolana and the Fe(OEt)₂ are both in solid phase; then there was the solid-liquid synthesis where the Fe(OEt)₂ was a liquid phase solution and pn-pozzolana still in solid phase. It was found that the conversion of the Fe(OEt)₂ deposited on the pn-pozzolana depended very significantly on its amount in relation to the pn of the pn-pozzolana. Thus, as the amount of the Fe(OEt)₂ increased, so its conversion and thus the deposit of the iron-Fe atoms on the pn-pozzolana was better. The ratio noted: “7×n”; where n was the moles numbers of the Fe(OEt)₂ on each monomer unit composing the pn; allowed to parameterize each tests. Thus, seeing that one mole of pn contains 7 moles of pn, hence the total number of the Fe(OEt)₂ deposited in an n-pn trial was "7×n". Consequently, it was shown that the radical mechanism of the iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO₂ by the intermediate of the Fe(OEt)₂ passed initially by the formation of an intermediate by dismutation of the neighboring molecules of the Fe(OEt)₂ with iron-Fe atoms depositions followed by the formation of a by-product “diethyl-peroxide” with other iron-Fe atoms depositions by which the reactions progress had been followed. This mechanism allowed to understand and explain the excellence of the iron-Fe atoms depositions on pn-pozzolana or pn-SiO₂. Thus, a kinetic study of this Fe(OEt)₂ on the pn-pozzolana followed by the iron-Fe atoms depositions had been carried out at 55°C with the optimum ratio "7×4" and allowed to evaluate and calculate the value of its rate constant of the order of 0.6841 [mol×l^-1×s^-1] with 2nd partial order in relation to the Fe(OEt)₂. Finally, some Fe-pn-pozzolana and Fe-pn-SiO₂ materials were synthesized followed by their characterizations in particular by xrf-spectrophotometer which made it possible to confirm the pn's role of the pn-pozzolana as support promoting the excellent iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO₂ by the intermediate of the ironIIethoxide Fe(OEt)₂ with weight dispersion and alkene rate in the order respectively of 5.11% à 23.02% and 5.59E-4 [mol×g^-1] to 8.91E-4 [mol×g^-1].

Published in	American Journal of Polymer Science and Technology (Volume 8, Issue 2)
DOI	10.11648/j.ajpst.20220802.12
Page(s)	28-37
Creative Commons	This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.
Copyright	Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Pn, Pozzolana, Pn-Pozzolana, Fe-pn-Pozzolana, Fe-Pn-SiO₂, IronIIethoxide-Fe(OEt)₂

References

[1]	Rabemananjara Marie Louise - ^«Synthèse de PN-pouzzolane et sa valorisation à l’adsorption des polymères marron d’acide citrique et en échangeur cationique PN-pouzzolane-Na^» - [Synthesis of PN-pouzzolan and its valorisation for the adsorption of citric acid brown polymers and in PN-pouzzolan-Na cationic exchanger] Mémoire de fin d’étude en vue de l’obtention du diplôme de master titre ingénieur en génie des procédés chimiques et industriels. Ecole Supérieure Polytechnique Antananarivo (E. S. P. A) – Université d’Antananarivo. 2018 - promotion 2018 – Soutenue le 10 Janvier 2020.
[2]	Andry Tahina Rabeharitsara, Nicole Rabemananjara, Nambinina Richard Randriana ^«Black Citric Acid Polymer (PN) Pozzolana Activated- Na-PN-Pozzolana-CE Material Synthesis Tested As Cationic Exchanger^» American Journal of Applied Chemistry; Volume 7, issue 6, December 2019, Pages: 145-160.
[3]	Sammy Eric Andriambola – ^«Valorisation de l’acide citrique en polymères et en sels de mono- di- et tri-ammonium^»-[Valorization of citric acid into polymers and mono-di- and tri-ammonium salts]. Mémoire de fin d’étude en vue de l’obtention du diplôme d’Ingénieur en Génie Chimique. E. S. P. A. Université d’Antananarivo. Promotion 2013.
[4]	Nicole Rabemananjara. ^«Test d’auto-inflammation du mélange polymère noir d’acide citrique (PN) et du fuel oil (FO) – Etude de la formation de coke^» - [Auto-ignition test of black polymer mixture of citric acid (PN) and fuel oil (FO) - Study of coke formation]. Mémoire de fin d’étude en vue de l’obtention du diplôme de Licence en génie des procédés chimiques et industriels. Ecole Supérieure Polytechnique Antananarivo (E. S. P. A) – Université d’Antananarivo. Promotion 2017 – Soutenue le 28 Mars 2017.
[5]	Andry Tahina Rabeharitsara, Nicole Rabemananjara, Nambinina Richard Randriana, Haritiana Jeannelle Rakotonirina, Edouard Andrianarison, André Razafimandefitra, Baholy Robijaona. ^«Auto-Inflammation Test of Black Citric Acid Polymer (PN) and Fuel Oil (FO) Mixes – Coke Formation^». American Journal of Applied Chemistry. Vol. 5, No. 3, June 2017. doi: 10.11648/j.ajac.20170503.11.
[6]	Marson Randrianomenjanahary Avotra – ^«La synthese au laboratoire de l’ethanolate de sodium, du citrate tri-sodium, de l’ethanolate de fer-II et du chlorure de fer-II avec de l’ethanol 90°^» - [Laboratory Synthesis of Sodium Ethanolate, Tri-Sodium Citrate, Iron II Ethanolate and Iron II Chloride With 90° Ethanol]. Mémoire de fin d’étude en vue de l’obtention du diplôme de Licence en génie des procédés chimiques et industriels. Ecole Supérieure Polytechnique Antananarivo (E. S. P. A) – Université d’Antananarivo - Promotion 2020 – Soutenu le 4 Août 2021.
[7]	Andry Tahina Rabeharitsara, Avotra Marson Randrianomenjanahary, Nambinina Richard Randriana, ^«Laboratory Synthesis and Titrations of IronIIchloride-FeCl₂ and IronII Ethoxide-Fe(OEt)₂ Using Ethanol-90°^» - Hexane and Sodium Ethoxide-Na (OEt)” American Journal of Applied Chemistry. Vol. 9, No. 5, August 2021, pp. 123-130. doi: 10.11648/j.ajac.20210905.11.
[8]	Aurélien Flura – ^«Réduction Sélective Catalytique Des Nox Par Des Composes Oxygénés^» - [Selective Catalytic Reduction Of Nox By Oxygenated Compounds]. Thèse pour l'obtention du Grade de Docteur De L'Université De Poitiers. Soutenue le 01 Juillet 2011.
[9]	Behevitra Rovatahianjanahary - « Synthèse de catalyseurs homogènes B_XH⁺ supportés sur les alcènes des aromatiques et des polynucléaires aromatiques oxygénés composant le bois du pin par traitement à l’acide sulfurique – Application dans la synthèse des polymères noires d’acide citrique » - [Synthesis of homogeneous B_XH⁺ catalysts supported on the alkenes of the aromatics and oxygenated aromatic polynuclei composing pine wood by treatment with sulfuric acid - Application in the synthesis of black polymers of citric acid]. Mémoire de fin d’étude en vue de l’obtention du diplôme de Licence en génie des procédés chimiques et industriels. Ecole Supérieure Polytechnique Antananarivo (E. S. P. A) – Université d’Antananarivo. Promotion 2018 – Soutenue le 26 Juillet 2018.
[10]	Andry Tahina Rabeharitsara, Behevitra Rovatahianjanahary, Nambinina Richard Randriana – «Pine Wood Powder Treatment To B_XH⁺ Homogeneous Catalyst (H⁺/H₂SO₄) Supported On Its Aromatics And PNA – Application In Black Citric Acid Polymer Synthesis». American Journal of Polymer Science and Technology. Vol. 4, No. 1, May 2018, pp. 1-27. doi: 10.11648/j.ajpst.20180401.11.
[11]	Andry Tahina Rabeharitsara, Phandry Nomena Ndjiva Rabearimihaja, – “Betacarotenes Dosage by Hydrofluoric Acid Solution and Validation of This New Process by SPC”. American Journal of Applied Chemistry. Vol. 4, No. 3, 2016, pp. 91-96. doi: 10.11648/j.ajac.20160403.14. Received: April 11, 2016; Accepted: April 20, 2016; Published: May 13, 2016.
[12]	Rabearimihaja Phandry Taryh Nomena Ndjiva - «Valorisation Du Betacarotene Extrait De L’huile De Palme Brute Par De L’acide Acetique Pour La Determination Des Teneurs En Eau De Produits Petroliers (Gazole /Fuel-Oil) Et Dosage Des Teneurs En Betacarotene Par De L’acide Fluorhydrique» - [Valorization of Betacarotene Extracted from Crude Palm Oil by Acetic Acid for the Determination of Water Content of Petroleum Products (Diesel/Fuel Oil) and Determination of Betacarotene Content by Hydrofluoric Acid]. Mémoire de fin d’Etudes en vue de l’obtention du Diplôme de Master Titre Ingénieur en Génie des Procédés chimiques et Industriels - Ecole Supérieure Polytechnique Antananarivo. Université d’Antananarivo – Promotion 2015 – Soutenue le 06 Mai 2016.

Cite This Article

Plain Text BibTeX RIS

APA Style

Andry Tahina Rabeharitsara, Ando Princia Randriamalala, Nambinina Richard Randriana, Baholy Robijaona, Marie Hanitriniaina Ratsimba. (2022). Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2. American Journal of Polymer Science and Technology, 8(2), 28-37. https://doi.org/10.11648/j.ajpst.20220802.12

Copy | Download

ACS Style

Andry Tahina Rabeharitsara; Ando Princia Randriamalala; Nambinina Richard Randriana; Baholy Robijaona; Marie Hanitriniaina Ratsimba. Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2. Am. J. Polym. Sci. Technol. 2022, 8(2), 28-37. doi: 10.11648/j.ajpst.20220802.12

Copy | Download

AMA Style

Andry Tahina Rabeharitsara, Ando Princia Randriamalala, Nambinina Richard Randriana, Baholy Robijaona, Marie Hanitriniaina Ratsimba. Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2. Am J Polym Sci Technol. 2022;8(2):28-37. doi: 10.11648/j.ajpst.20220802.12

Copy | Download

@article{10.11648/j.ajpst.20220802.12,
  author = {Andry Tahina Rabeharitsara and Ando Princia Randriamalala and Nambinina Richard Randriana and Baholy Robijaona and Marie Hanitriniaina Ratsimba},
  title = {Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2},
  journal = {American Journal of Polymer Science and Technology},
  volume = {8},
  number = {2},
  pages = {28-37},
  doi = {10.11648/j.ajpst.20220802.12},
  url = {https://doi.org/10.11648/j.ajpst.20220802.12},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ajpst.20220802.12},
  abstract = {The valorization of pozzolana into pn-pozzolana used as water softening was studied. This article treated particularly the valorization of the pn-pozzolana and pn-SiO2 by adding iron-Fe atoms to give the Fe-pn-pozzolana and Fe-pn-SiO2. Two synthesis procedures were used with the ironIIethoxide Fe(OEt)2 as precursor material of the iron-Fe atoms deposits on the pn-pozzolana: first there was the solid-solid synthesis where the pn-pozzolana and the Fe(OEt)2 are both in solid phase; then there was the solid-liquid synthesis where the Fe(OEt)2 was a liquid phase solution and pn-pozzolana still in solid phase. It was found that the conversion of the Fe(OEt)2 deposited on the pn-pozzolana depended very significantly on its amount in relation to the pn of the pn-pozzolana. Thus, as the amount of the Fe(OEt)2 increased, so its conversion and thus the deposit of the iron-Fe atoms on the pn-pozzolana was better. The ratio noted: “7×n”; where n was the moles numbers of the Fe(OEt)2 on each monomer unit composing the pn; allowed to parameterize each tests. Thus, seeing that one mole of pn contains 7 moles of pn, hence the total number of the Fe(OEt)2 deposited in an n-pn trial was "7×n". Consequently, it was shown that the radical mechanism of the iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the Fe(OEt)2 passed initially by the formation of an intermediate by dismutation of the neighboring molecules of the Fe(OEt)2 with iron-Fe atoms depositions followed by the formation of a by-product “diethyl-peroxide” with other iron-Fe atoms depositions by which the reactions progress had been followed. This mechanism allowed to understand and explain the excellence of the iron-Fe atoms depositions on pn-pozzolana or pn-SiO2. Thus, a kinetic study of this Fe(OEt)2 on the pn-pozzolana followed by the iron-Fe atoms depositions had been carried out at 55°C with the optimum ratio "7×4" and allowed to evaluate and calculate the value of its rate constant of the order of 0.6841 [mol×l-1×s-1] with 2nd partial order in relation to the Fe(OEt)2. Finally, some Fe-pn-pozzolana and Fe-pn-SiO2 materials were synthesized followed by their characterizations in particular by xrf-spectrophotometer which made it possible to confirm the pn's role of the pn-pozzolana as support promoting the excellent iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the ironIIethoxide Fe(OEt)2 with weight dispersion and alkene rate in the order respectively of 5.11% à 23.02% and 5.59E-4 [mol×g-1] to 8.91E-4 [mol×g-1].},
 year = {2022}
}

Copy | Download

TY  - JOUR
T1  - Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2
AU  - Andry Tahina Rabeharitsara
AU  - Ando Princia Randriamalala
AU  - Nambinina Richard Randriana
AU  - Baholy Robijaona
AU  - Marie Hanitriniaina Ratsimba
Y1  - 2022/08/05
PY  - 2022
N1  - https://doi.org/10.11648/j.ajpst.20220802.12
DO  - 10.11648/j.ajpst.20220802.12
T2  - American Journal of Polymer Science and Technology
JF  - American Journal of Polymer Science and Technology
JO  - American Journal of Polymer Science and Technology
SP  - 28
EP  - 37
PB  - Science Publishing Group
SN  - 2575-5986
UR  - https://doi.org/10.11648/j.ajpst.20220802.12
AB  - The valorization of pozzolana into pn-pozzolana used as water softening was studied. This article treated particularly the valorization of the pn-pozzolana and pn-SiO2 by adding iron-Fe atoms to give the Fe-pn-pozzolana and Fe-pn-SiO2. Two synthesis procedures were used with the ironIIethoxide Fe(OEt)2 as precursor material of the iron-Fe atoms deposits on the pn-pozzolana: first there was the solid-solid synthesis where the pn-pozzolana and the Fe(OEt)2 are both in solid phase; then there was the solid-liquid synthesis where the Fe(OEt)2 was a liquid phase solution and pn-pozzolana still in solid phase. It was found that the conversion of the Fe(OEt)2 deposited on the pn-pozzolana depended very significantly on its amount in relation to the pn of the pn-pozzolana. Thus, as the amount of the Fe(OEt)2 increased, so its conversion and thus the deposit of the iron-Fe atoms on the pn-pozzolana was better. The ratio noted: “7×n”; where n was the moles numbers of the Fe(OEt)2 on each monomer unit composing the pn; allowed to parameterize each tests. Thus, seeing that one mole of pn contains 7 moles of pn, hence the total number of the Fe(OEt)2 deposited in an n-pn trial was "7×n". Consequently, it was shown that the radical mechanism of the iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the Fe(OEt)2 passed initially by the formation of an intermediate by dismutation of the neighboring molecules of the Fe(OEt)2 with iron-Fe atoms depositions followed by the formation of a by-product “diethyl-peroxide” with other iron-Fe atoms depositions by which the reactions progress had been followed. This mechanism allowed to understand and explain the excellence of the iron-Fe atoms depositions on pn-pozzolana or pn-SiO2. Thus, a kinetic study of this Fe(OEt)2 on the pn-pozzolana followed by the iron-Fe atoms depositions had been carried out at 55°C with the optimum ratio "7×4" and allowed to evaluate and calculate the value of its rate constant of the order of 0.6841 [mol×l-1×s-1] with 2nd partial order in relation to the Fe(OEt)2. Finally, some Fe-pn-pozzolana and Fe-pn-SiO2 materials were synthesized followed by their characterizations in particular by xrf-spectrophotometer which made it possible to confirm the pn's role of the pn-pozzolana as support promoting the excellent iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the ironIIethoxide Fe(OEt)2 with weight dispersion and alkene rate in the order respectively of 5.11% à 23.02% and 5.59E-4 [mol×g-1] to 8.91E-4 [mol×g-1].
VL  - 8
IS  - 2
ER  -

Copy | Download

Author Information

Andry Tahina Rabeharitsara

Chemical Process Engineering Department (Ecole Supérieure Polytechnique Antananarivo – E.S.P.A), Antananarivo University, Antananarivo, Madagascar
Ando Princia Randriamalala

Chemical Process Engineering Department (Ecole Supérieure Polytechnique Antananarivo – E.S.P.A), Antananarivo University, Antananarivo, Madagascar
Nambinina Richard Randriana

Chemical Process Engineering Department (Ecole Supérieure Polytechnique Antananarivo – E.S.P.A), Antananarivo University, Antananarivo, Madagascar
Baholy Robijaona

Chemical Process Engineering Department (Ecole Supérieure Polytechnique Antananarivo – E.S.P.A), Antananarivo University, Antananarivo, Madagascar
Marie Hanitriniaina Ratsimba

Chemical Process Engineering Department (Ecole Supérieure Polytechnique Antananarivo – E.S.P.A), Antananarivo University, Antananarivo, Madagascar

Download PDF

Sections

Plain Text BibTeX RIS

APA Style

Andry Tahina Rabeharitsara, Ando Princia Randriamalala, Nambinina Richard Randriana, Baholy Robijaona, Marie Hanitriniaina Ratsimba. (2022). Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2. American Journal of Polymer Science and Technology, 8(2), 28-37. https://doi.org/10.11648/j.ajpst.20220802.12

Copy | Download

ACS Style

Andry Tahina Rabeharitsara; Ando Princia Randriamalala; Nambinina Richard Randriana; Baholy Robijaona; Marie Hanitriniaina Ratsimba. Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2. Am. J. Polym. Sci. Technol. 2022, 8(2), 28-37. doi: 10.11648/j.ajpst.20220802.12

Copy | Download

AMA Style

Andry Tahina Rabeharitsara, Ando Princia Randriamalala, Nambinina Richard Randriana, Baholy Robijaona, Marie Hanitriniaina Ratsimba. Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2. Am J Polym Sci Technol. 2022;8(2):28-37. doi: 10.11648/j.ajpst.20220802.12

Copy | Download

@article{10.11648/j.ajpst.20220802.12,
  author = {Andry Tahina Rabeharitsara and Ando Princia Randriamalala and Nambinina Richard Randriana and Baholy Robijaona and Marie Hanitriniaina Ratsimba},
  title = {Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2},
  journal = {American Journal of Polymer Science and Technology},
  volume = {8},
  number = {2},
  pages = {28-37},
  doi = {10.11648/j.ajpst.20220802.12},
  url = {https://doi.org/10.11648/j.ajpst.20220802.12},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ajpst.20220802.12},
  abstract = {The valorization of pozzolana into pn-pozzolana used as water softening was studied. This article treated particularly the valorization of the pn-pozzolana and pn-SiO2 by adding iron-Fe atoms to give the Fe-pn-pozzolana and Fe-pn-SiO2. Two synthesis procedures were used with the ironIIethoxide Fe(OEt)2 as precursor material of the iron-Fe atoms deposits on the pn-pozzolana: first there was the solid-solid synthesis where the pn-pozzolana and the Fe(OEt)2 are both in solid phase; then there was the solid-liquid synthesis where the Fe(OEt)2 was a liquid phase solution and pn-pozzolana still in solid phase. It was found that the conversion of the Fe(OEt)2 deposited on the pn-pozzolana depended very significantly on its amount in relation to the pn of the pn-pozzolana. Thus, as the amount of the Fe(OEt)2 increased, so its conversion and thus the deposit of the iron-Fe atoms on the pn-pozzolana was better. The ratio noted: “7×n”; where n was the moles numbers of the Fe(OEt)2 on each monomer unit composing the pn; allowed to parameterize each tests. Thus, seeing that one mole of pn contains 7 moles of pn, hence the total number of the Fe(OEt)2 deposited in an n-pn trial was "7×n". Consequently, it was shown that the radical mechanism of the iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the Fe(OEt)2 passed initially by the formation of an intermediate by dismutation of the neighboring molecules of the Fe(OEt)2 with iron-Fe atoms depositions followed by the formation of a by-product “diethyl-peroxide” with other iron-Fe atoms depositions by which the reactions progress had been followed. This mechanism allowed to understand and explain the excellence of the iron-Fe atoms depositions on pn-pozzolana or pn-SiO2. Thus, a kinetic study of this Fe(OEt)2 on the pn-pozzolana followed by the iron-Fe atoms depositions had been carried out at 55°C with the optimum ratio "7×4" and allowed to evaluate and calculate the value of its rate constant of the order of 0.6841 [mol×l-1×s-1] with 2nd partial order in relation to the Fe(OEt)2. Finally, some Fe-pn-pozzolana and Fe-pn-SiO2 materials were synthesized followed by their characterizations in particular by xrf-spectrophotometer which made it possible to confirm the pn's role of the pn-pozzolana as support promoting the excellent iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the ironIIethoxide Fe(OEt)2 with weight dispersion and alkene rate in the order respectively of 5.11% à 23.02% and 5.59E-4 [mol×g-1] to 8.91E-4 [mol×g-1].},
 year = {2022}
}

Copy | Download

TY  - JOUR
T1  - Valorization of the Pn-Pozzolana to the Synthesis of Fe-pn-Pozzolana Study - Application to the Synthesis of the Fe-Pn-SiO2
AU  - Andry Tahina Rabeharitsara
AU  - Ando Princia Randriamalala
AU  - Nambinina Richard Randriana
AU  - Baholy Robijaona
AU  - Marie Hanitriniaina Ratsimba
Y1  - 2022/08/05
PY  - 2022
N1  - https://doi.org/10.11648/j.ajpst.20220802.12
DO  - 10.11648/j.ajpst.20220802.12
T2  - American Journal of Polymer Science and Technology
JF  - American Journal of Polymer Science and Technology
JO  - American Journal of Polymer Science and Technology
SP  - 28
EP  - 37
PB  - Science Publishing Group
SN  - 2575-5986
UR  - https://doi.org/10.11648/j.ajpst.20220802.12
AB  - The valorization of pozzolana into pn-pozzolana used as water softening was studied. This article treated particularly the valorization of the pn-pozzolana and pn-SiO2 by adding iron-Fe atoms to give the Fe-pn-pozzolana and Fe-pn-SiO2. Two synthesis procedures were used with the ironIIethoxide Fe(OEt)2 as precursor material of the iron-Fe atoms deposits on the pn-pozzolana: first there was the solid-solid synthesis where the pn-pozzolana and the Fe(OEt)2 are both in solid phase; then there was the solid-liquid synthesis where the Fe(OEt)2 was a liquid phase solution and pn-pozzolana still in solid phase. It was found that the conversion of the Fe(OEt)2 deposited on the pn-pozzolana depended very significantly on its amount in relation to the pn of the pn-pozzolana. Thus, as the amount of the Fe(OEt)2 increased, so its conversion and thus the deposit of the iron-Fe atoms on the pn-pozzolana was better. The ratio noted: “7×n”; where n was the moles numbers of the Fe(OEt)2 on each monomer unit composing the pn; allowed to parameterize each tests. Thus, seeing that one mole of pn contains 7 moles of pn, hence the total number of the Fe(OEt)2 deposited in an n-pn trial was "7×n". Consequently, it was shown that the radical mechanism of the iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the Fe(OEt)2 passed initially by the formation of an intermediate by dismutation of the neighboring molecules of the Fe(OEt)2 with iron-Fe atoms depositions followed by the formation of a by-product “diethyl-peroxide” with other iron-Fe atoms depositions by which the reactions progress had been followed. This mechanism allowed to understand and explain the excellence of the iron-Fe atoms depositions on pn-pozzolana or pn-SiO2. Thus, a kinetic study of this Fe(OEt)2 on the pn-pozzolana followed by the iron-Fe atoms depositions had been carried out at 55°C with the optimum ratio "7×4" and allowed to evaluate and calculate the value of its rate constant of the order of 0.6841 [mol×l-1×s-1] with 2nd partial order in relation to the Fe(OEt)2. Finally, some Fe-pn-pozzolana and Fe-pn-SiO2 materials were synthesized followed by their characterizations in particular by xrf-spectrophotometer which made it possible to confirm the pn's role of the pn-pozzolana as support promoting the excellent iron-Fe atoms depositions on the pn-pozzolana or the pn-SiO2 by the intermediate of the ironIIethoxide Fe(OEt)2 with weight dispersion and alkene rate in the order respectively of 5.11% à 23.02% and 5.59E-4 [mol×g-1] to 8.91E-4 [mol×g-1].
VL  - 8
IS  - 2
ER  -

Copy | Download